MRS Proceedings, Cambridge University Press, Volume 766, New York, USA (2003)

URL:

https://www.cambridge.org/core/article/div-class-title-creating-nanoporosity-by-selective-extraction-of-porogens-using-supercritical-carbon-dioxide-cosolvent-processes-div/6995C75C6A7BE6F356416D0F189364F8

Abstract:

AbstractThis work presents a novel approach using supercritical carbon dioxide (SCCO2) to selectively extract poly(propylene glycol) (PPG) porogen from a poly(methylsilsesquioxane) (PMSSQ) matrix, which results in the formation of nanopores. Nanoporous thin films were prepared by spin-casting a solution containing appropriate quantities of PPG porogen and PMSSQ dissolved in PM acetate. The as-spun films were thermally cured at temperatures well below the thermal degradation temperature of the organic polymer to form a cross-linked organic/inorganic polymer hybrid. By selectively removing the CO2 soluble PPG porogen, open and closed pore structures are possible depending upon the porogen load and its distribution in the matrix before extraction. In the present work, two different loadings of PPG namely 25 wt.% and 55 wt.% were used. Both static SCCO2 and pulsed SCCO2/cosolvent treatments were used for PPG extraction. The initial results indicate that the pulsed SCCO2/cosolovent treatm" # "ent was more efficient. Fourier transform infrared spectroscopy (FTIR) and refractive index measurements further corroborate the successful extraction of the porogens at relatively low temperatures (2000C). For the pure PMSSQ film, the k value is 3.1, whereas it is 1.46 and 2.27 for the open and closed pore compositions respectively after the static SCCO2 extraction and 430°C subsequent annealing. The reduction in the k-value is attributed to the formation of nanopores. The pore structure was verified from transmission electron microscopy (TEM), and from small-angle x-ray scattering (SAXS) measurements, the pore size was determined to be 1-3 nm for these films.

Cite this Research Publication

B. Lahlouh, Dr. T. Rajagopalan, Lubguban, J. A., Biswas, N., Gangopadhyaya, S., Sun, J., Huang, D., Simon, S. L., Kim, H. C., Volksen, W., and Miller, R. D., “Creating Nanoporosity by Selective Extraction of Porogens Using Supercritical Carbon Dioxide/Cosolvent Processes”, MRS Proceedings, vol. 766, 2003.

207
PROGRAMS
OFFERED
6
AMRITA
CAMPUSES
15
CONSTITUENT
SCHOOLS
A
GRADE BY
NAAC, MHRD
8th
RANK(INDIA):
NIRF 2018
150+
INTERNATIONAL
PARTNERS