Surface modification of HDPE and PP by mechanical polishing and DC glow discharge and their adhesive joining to steel

Publication Type : Journal Article

Publisher : Wiley Online Library

Source : Journal of applied polymer science, Wiley Online Library, Volume 80, Number 8, p.1140–1149 (2001)

Keywords : Adhesive Joining, DC glow discharge, HDPE, Joint Strength, Mechanical Polishing, PP, Surface energy

Campus : Coimbatore

School : Department of Aerospace Engineering, School of Engineering

Department : Aerospace

Year : 2001

Abstract : To improve the strengths of the adhesive joints of high density polyethylene (HDPE) and polypropylene (PP) to steel, the surfaces of HDPE and PP sheets have been treated by DC glow discharge to increase the polar component of surface energy significantly. Present study investigates the effect of mechanical polishing prior to surface modification of substrates of HDPE and PP sheets by exposure to DC glow discharge, on the surface energy and their adhesive joint strength to steel. The mechanical polishing has been carried out by abrading with 120, 220, 400, 600, 800, and 1000 grade emery paper of grit sizes 8.33, 4.54, 2.5, 1.67, 1.2, and 1 micron, respectively. The surface energy of a given surface has been evaluated by measuring contact angles of sessile drops of two test liquids of known surface tension components, such as deionized water and formamide. It is observed that 800-grade emery paper of grit size 1.2 micron has been found most effective in terms of their reduction in contact angles and enhancement of their surface energies. The change in surface energy due to surface modification has also been evaluated by measuring the surface energies of unpolished sheets exposed to DC glow discharge. The surface modification of the polymers by glow discharge for 120 s at a power level of 13 W decreases the contact angle more on mechanically polished specimens than that observed on unpolished sheets. Due to glow discharge treatment, the polar component of surface energy increases significantly in HDPE and PP, especially when they are mechanically polished (800 grade) prior to glow discharge. However, in case of the HDPE sheets, the effect of glow discharge on the polar component of surface energy is significantly higher compared to that for dispersion component of surface energy, whereas the polar component of surface energy of the PP sheet is lower than the dispersion component of surface energy. But in both the cases, mechanical polishing prior to glow discharge appears to affect the polar component of surface energy. Mechanical polishing of the HDPE and PP sheets by abrading with 800-grade emery paper prior to glow discharge treatment, increases the adhesive joint strengths over those observed in case of unpolished polymers exposed to glow discharge. However, the use of prior mechanical polishing increases the joint strength only by a little more than 10% compared to a five to seven times increase in strength observed as a consequence of exposure to glow discharge of as received samples.