Highly Reactive Crystalline (001) Facet of BiI3 Hexagonal Nanoplates for Visible Light Photodetectors

Publication Type : Journal Article

Publisher : American Chemical Society

Source : ACS Applied Electronic Materials, 2023

Url : https://pubs.acs.org/doi/abs/10.1021/acsaelm.3c00433

Campus : Coimbatore

School : School of Engineering, School of Physical Sciences

Department : Sciences

Year : 2023

Abstract : A simple and facile solution phase synthesis of large-scale, micro-to-nanometer sized bismuth triiodide (BiI3) single crystalline hexagonal plates is reported. It is demonstrated that under optimized conditions the reactions result in dominant exposed (001) facets. Because of the large size, high surface-to-volume ratio, and thickness, BiI3 nanoplatelets are attractive as visible light photodetectors. At 1 V bias, the photoresponsivity is 0.87 A W–1; the specific detectivity is 4.8 × 1012 jones with a response rise time of 1 s and a fall time of 0.97 s. The Kelvin probe force microscope images revealed that the surface potential difference across the junction was 42.5 mV, which is attributed to the work function difference between the sample and substrate. The results of this study indicate that single hexagonal platelets of BiI3 are very promising for visible light photodetector applications.

Cite this Research Publication : Durga Prasad Muvva, Sudip Kumar Batabyal, Ghanashyam Krishna Mamidipudi, "Highly Reactive Crystalline (001) Facet of BiI3 Hexagonal Nanoplates for Visible Light Photodetectors", ACS Applied Electronic Materials, 2023