Publication

Abstract : This work assesses the frictional wear of lubricated transmission chains, correlating the coefficient of friction, root mean square (RMS) acoustic emissions, and vibrations induced by friction, incorporating Industrial Internet of Things (IIoT) components. The work is divided into two phases: understanding the frictional interactions between the steel pins of commercial transmission chain and high chrome steel plate (mimicking the interaction between the pin and roller of the chain) using a reciprocating tribometer (20 N, 2.5 Hz, 15.1 stroke length) in the presence of three commercial lubricant aerosols (Grade A, Grade B, and Grade C) and analyzing the frictional wear, sound, and vibration signals generated during the tribo-tests. In the second phase, the findings from the laboratory scale are validated using a commercial transmission chain under aerosol lubrication. Results indicated that the coefficient of friction in the case of dry conditions was 41% higher than that of Grade A aerosol and Grade C aerosol and 28% higher than that of Grade B aerosol. However, the average wear scar diameter on the pin with Grade C (0.401 ± 0.129 mm) was higher than that on the pins with Grades A (0.209 ± 0.159 mm) and B (0.204 ± 0.165 mm). Grade A and Grade B aerosols exhibited similar frictional conditions, while the wear-scar diameter in Grade C was the highest among Grades A and B but still less than in dry conditions. Analyzing the sound and vibrations generated during the friction test, it can be seen that the dry condition produced approximately 60% more sound level than the Grade A and Grade B conditions, and 41% more sound than the Grade C condition. The laboratory results were validated with a real-time transmission chain using an in-house chain wear test rig. Results from the chain wear test rig indicated that the elongation of the chain with Grade B is the least amongst the aerosols and dry conditions. The surface characterizations of the steel pins also indicated intense deep grooves and surface damage in dry conditions, with Grade A exhibiting the most severe damage, followed by Grade C, and the least severe in Grade B. Additionally, dark patches were visually observed on the rollers of the lubricated commercial chains, indicating stressed areas on the rollers, while polished wear was observed on the rollers under dry conditions.